标题: designspace 6.1 [打印本页]

作者: twfjup2 时间: 2003-10-22 14:21
标题: designspace 6.1
我用 designspace 6.1 分析 PA66的胶件

不知道 young's modulus 是多少

谁能告诉我吗

谢谢

作者: LKK52 时间: 2003-10-22 16:07
https://matweb.com/search/searchsubcat.asp

作者: twfjup2 时间: 2003-10-22 16:33
谢谢了
DuPont Zytel GRZ 70G13L Nylon 66, 13% Short Glass Fibers, Dry As Molded

ensile Strength, Ultimate  121 MPa  17500 psi  
Elongation at Break  3 %  3 %  
Flexural Modulus  4.826 GPa  700 ksi  
Flexural Yield Strength  165 MPa  23900 psi  
Shear Strength  76 MPa  11000 psi  
Izod Impact, Notched  0.48 J/cm  0.899 ft-lb/in  

没有 young's modulus 啊